Polycarbonate (PC) |
|
|
|
|
|
|
|
牌号 |
熔值 |
密度 |
收缩率 |
拉伸
强度 |
缺口冲
击强度 |
热变形温度 |
阻燃性能 |
|
Application |
Test Method |
D792 |
D955 |
D638 |
D790 |
D256 |
D648 |
|
|
|
Unit |
g/cm3 |
% |
Mpa |
Mpa |
J/M |
℃ （1.82MPa） |
1/16” |
1/8“ |
|
Flame retardant |
|
PC-000/000 FR V0 TP |
1.20 |
0.5-0.7 |
60 |
2450 |
620 |
120 |
— |
V-0 |
Flame retardant and transparent |
PC-000/000 FR V0 WT |
1.26 |
0.5-0.7 |
60 |
2450 |
600 |
120 |
V-0 |
V-0 |
Flame retardant |
PC-000/10T FR |
1.25 |
0.5-0.7 |
50 |
2000 |
160 |
120 |
V-0 |
V-0 |
Flame retardant with 10% PTFE lubricant |
PC-10GF/000 FR |
1.27 |
0.2-0.4 |
75 |
4100 |
80 |
130 |
V-0 |
V-0 |
Flame retardant with 10% GF reinforced |
PC-15GF/10T FR |
1.37 |
0.2-0.4 |
75 |
4000 |
80 |
135 |
V-0 |
V-0 |
Flame retardant with 10% GF and 10% PTFE |
PC-20GF/000 FR |
1.36 |
0.1-0.3 |
115 |
7200 |
115 |
140 |
V-0 |
V-0 |
Flame retardant with 20% GF reinforced |
PC-30GF/000 FR |
1.45 |
0.1-0.3 |
120 |
10000 |
130 |
140 |
V-0 |
V-0 |
Flame retardant with 30% GF reinforced |
PC-10CF/000 FR |
1.24 |
0.2-0.3 |
115 |
8500 |
65 |
130 |
V-0 |
V-0 |
Flame retardant with 10 carbon fibre reinforced |
Lubricant |
|
PC-000/05T |
1.24 |
0.5-0.7 |
58 |
2400 |
120 |
125 |
HB |
HB |
5% PTFE lubricant |
PC-000/10T |
1.26 |
0.5-0.7 |
56 |
2300 |
120 |
125 |
HB |
HB |
10% PTFE lubricant |
PC-000/15T |
1.28 |
0.5-0.7 |
55 |
2300 |
110 |
130 |
HB |
HB |
15% PTFE lubricant |
PC-000/20T |
1.32 |
0.5-0.7 |
45 |
2200 |
110 |
130 |
HB |
HB |
20% PTFE lubricant |
PC-10GF/10 |
1.38 |
0.2-0.4 |
70 |
3100 |
90 |
135 |
— |
HB |
10GF reinforced with 10% PTFE lubricant |
PC-10GF/20T |
1.39 |
0.2-0.4 |
90 |
3450 |
100 |
137 |
— |
HB |
10GF reinforced with 20% PTFE lubricant |
PC-15GF/10T |
1.37 |
0.2-0.4 |
90 |
4000 |
95 |
140 |
— |
HB |
15GF reinforced with 15% PTFE lubricant |
PC-15GF/20T |
1.44 |
0.2-0.4 |
85 |
4800 |
95 |
140 |
— |
HB |
15GF reinforced with 20% PTFE lubricant |
PC-30GF/5T |
1.46 |
0.2-0.3 |
105 |
8500 |
100 |
136 |
— |
HB |
30GF reinforced with 5% PTFE lubricant |
PC-10CF/5T |
1.27 |
0.3-0.5 |
110 |
7000 |
75 |
140 |
— |
HB |
10% carbon fibre reinforced with 5% PTFE lubricant |
PC-10CF/15T |
1.32 |
0.3-0.4 |
110 |
6500 |
110 |
140 |
— |
HB |
10% carbon fibre reinforced with 15% PTFE lubricant |
PC-10CF-10GF/10T |
1.38 |
0.2-0.3 |
110 |
6800 |
65 |
135 |
— |
HB |
10% carbon fibre and 10 GF reinforced with 10% PTFE lubricant |
PC-20CF/15T |
1.36 |
0.2-0.3 |
120 |
9000 |
60 |
140 |
— |
HB |
20% carbon fibre reinforced with 10% PTFE lubricant |
PC-30CF/15T |
1.43 |
0.2-0.3 |
150 |
15000 |
60 |
140 |
— |
HB |
30% carbon fibre reinforced with 10% PTFE lubricant |
Glass fibre reinforced |
PC-10GF/000 |
1.25 |
0.4-0.6 |
70 |
4100 |
100 |
140 |
— |
HB |
10% GF reinforced |
PC-20GF/000 |
1.34 |
0.2-0.4 |
110 |
5500 |
110 |
145 |
— |
HB |
20% GF reinforced |
PC-30GF/000 |
1.43 |
0.1-0.2 |
130 |
9000 |
130 |
145 |
— |
HB |
30% GF reinforced |
PC-40GF/000 |
1.50 |
0.1-0.2 |
150 |
10000 |
150 |
145 |
— |
HB |
40% GF reinforced |
Carbon fibre reinfoced |
PC-10CF/000 |
1.24 |
0.3-0.5 |
120 |
8500 |
60 |
140 |
— |
HB |
10% carbon fibre reinforced |
PC-15CF/000 |
1.27 |
0.2-0.3 |
130 |
10000 |
70 |
140 |
— |
HB |
15% carbon fibre reinforced |
PC-20CF/000 |
1.29 |
0.2-0.3 |
137 |
11000 |
75 |
143 |
— |
HB |
20% carbon fibre reinforced |
PC-30CF/000 |
1.33 |
0.2~0.3 |
160 |
13000 |
80 |
146 |
— |
HB |
30% carbon fibre reinforced |